Natrijum silikatno staklo kao novi fazno izmenljivi materijal - ispitivanja i primena

Autor

Bijelić, Ivan, 1975-

Doprinosi

Tadić, Branko, 1958-
Vukelić, Đorđe, 1974-
Živić, Fatima, 1970-
Adamović, Dragan, 1960-

Opis (srp)

Rezultati istraživanja izloženi u ovoj disertaciji u osnovi pripadajuoblasti steznih pribora. Odnose se, na danas veoma aktuelnu oblast faznoizmenljivih pribora koji se primenjuju u operacijama mašinske obrade tankozidnihelemenata složene konfiguracije, kod kojih su maksimalno izraženi problemiotežanog baziranja i stezanja i postizanja zahtevanog kvaliteta obrade. Izloženateorijska i eksperimentalna istraživanja, više od pet godina unazad, prateoriginalnu ideju da se natrijum silikatno staklo uvede u tehnologije dizajniranjasteznih pribora kao novi fazno izmenljivi materijal. Opsežnim pregledomliteraturnih izvora vezanih za postojeće fazno izmenljive materijale, i obimnimprogramom eksperimentalih ispitivanja izvedenih na modelima i namenskiprojektovanim i realizovanim uređajima za ispitivanja uzoraka, u statičkim idinamičkim uslovima opterećenja, utvrđeno je da se natrijum silikatno staklo veomaefikasno može primeniti kao novi fazno izmenljivi materijal. Po mišljenju autoradisertacije primena natrijum silikatnog stakla kao novog fazno izmenljivogmaterijala najveće tehno-ekonomske efekte može dati u operacijama izrade dubokihdžepova. Rezultati publikovanih istraživanja autora ove disertacije [1] pokazuju da jeprimenom natrijum silikatnog stakla uspešno izvedena izrada dubokog džepa, odnosavisine džepa i debljine zida složene konture, jednakoj vrednosti 417. Što je, u odnosuna literaturne podatke [2] neuporedivo veća vrednost od do sada ostvarenihvrednosti. Pri čemu rezultati teorijskih analiza, izvedenih numeričkih proračuna iCAD inspekcija više uzoraka izrađenog dubokog džepa ukazuju na veoma povoljnuraspodelu naponskih i deformacionih polja i visoku tačnost izrade. Treba naglasitii to, da je natrijum silikatno staklo veoma dostupan materijal niske cene koštanjakoji pomešan sa šamotnim brašnom očvršćava na sobnoj i povišenim temperaturamai poprima svojstva kamena dok se u drugoj fazi jednostavno rastvara u vodi.

Opis (srp)

-

Opis (eng)

The research results presented in this dissertation basically belong to the field offixture design. They relate to today's very current field of phase-changeable fixtures that areused in machining operations of thin-walled elements of complex configuration, where theproblems of difficult basing and clamping and achieving the required quality of machining aremaximally expressed. The presented theoretical and experimental research, more than fiveyears ago, follows the original idea to introduce natrium silicate glass into the technologies ofdesigning of fixtures as a new phase-changeable material. An extensive review of literaturesources related to existing phase-change materials, and an extensive program of experimentaltests performed on models and specially designed and realized devices for testing samples, instatic and dynamic load conditions, determined that natrium silicate glass can be veryeffectively applied as a new phase-change material. In the opinion of the author of thisdissertation, the application of natrium silicate glass as a new phase-changeable material cangive the greatest techno-economic effects in the operations of making deep pockets. Theresults of the published research of the author of this dissertation [1] show that the machiningof a deep pocket was successfully performed using natrium silicate glass, the ratio of theheight of the pocket and the thickness of the wall of a complex contour equal to the value of417. Which, in relation to the literature data [2] is an incomparably higher value than thevalues achieved so far. The results of theoretical analyses, performed numerical calculationsand CAD inspections of the several machined deep pocket samples indicate a very favorabledistribution of stress and deformation fields and high manufacturing accuracy. It should alsobe emphasized that natrium silicate glass is a very available, low-cost material that, mixedwith fireclay flour, hardens at room and higher temperatures and takes on the properties ofstone, while in the second phase it simply dissolves in water.

Jezik

srpski

Datum

2023

Licenca

Ovo delo je licencirano pod uslovima licence
Creative Commons CC BY-ND 3.0 AT - Creative Commons Autorstvo - Bez prerada Austria License.

http://creativecommons.org/licenses/by-nd/3.0/at/legalcode